釔安定氧化鋯粉
產品說明
| Y2O3 Stabilized Zirconia 氧化釔安定化氧化鋯粉 | |||||||||
| Powder Characterisitics and Properties | |||||||||
| TZ-3Y-E (TZ-3YB-E) |
TZ-3YS-E (TZ-3YSB-E) (TZ-3YSB-C) |
TZ-4Y | TZ-6Y | TZ-8Y | TZ-10Y | TZ-3Y20A (TZ-3Y20AB) |
Zpex | TZ-Black (TZ-Black-B) |
|
| Y2O3 (mol.%) | 3 | 3 | 4 | 6 | 8 | 10 | 3 | 3 | 3 |
| Actual Particle Size(μm) | 0.04 (40nm) |
0.09 (90nm) |
0.04(40nm) | - | 0.04 (40nm) |
0.09 (90nm) |
|||
| Powder Characteristics | |||||||||
| Y2O3(wt%) | 5.2±0.5 | 7.0±0.6 | 10.3±0.6 | 13.3±0.6 | 15.9±0.7 | 3.9±0.3 | 5.35±0.2 | 5.0±1.0 | |
| HfO2(wt%) | <5.0 | ||||||||
| Al2O3(wt%) | 0.1~0.4 | ≦0.1 | 18~22 | ≦0.1 | -- | ||||
| SiO2(wt%) | ≦0.02 | ≦0.05 | |||||||
| Fe2O3(wt%) | ≦0.01 | -- | |||||||
| Na2O(wt%) | ≦0.04 | ≦0.06 | ≦0.12 | ≦0.04 | |||||
| Pigment(wt%) | -- | ≦5.0 | |||||||
| Specific Surface Area (m2/g) | 16±3 | 7±2 | 16±3 | 13±3 | 15±3 | 13±3 | 10±3 | ||
| Typical Properties of Sinterdd Body | |||||||||
| Density(g/cm3) | 6.05 | 6.02 | 5.90 | 5.80 | 5.50 | 6.08 | 6.00 | ||
| Bending Strength R.T.(MPa)*1 | 1200 | 1000 | 500 | 300 | 200 | 2000 (HIPing) |
1100 | 1200 | |
| Hardness (Hv10)*2 | 1250 | 1400 | 1250 | 1200 | |||||
*2:JIS R1610 (Loads:98.07N)